Nanostructured Lead Electrodes with Reduced Graphene Oxide for High-Performance Lead–Acid Batteries
2022
Nanostructured Pb electrodes consisting of nanowire arrays were obtained by electrodeposition, to be used as negative electrodes for lead–acid batteries. Reduced graphene oxide was added to improve their performances. This was achieved via the electrochemical reduction of graphene oxide directly on the surface of nanowire arrays. The electrodes with and without reduced graphene oxide were tested in a 5 M sulfuric acid solution using a commercial pasted positive plate and an absorbed glass mat separator in a zero-gap configuration. The electrodes were tested in deep cycling conditions with a very low cut-off potential. Charge–discharge tests were performed at 5C. The electrode wi…
Nanostructured lead-acid negative electrode with reduced graphene oxide
2021
Aim of this work is to develop a new nano-structured and nano-composite lead acid negative electrode with reduced graphene oxide (rGO). Nanostructured electrodes are fabricated by template electrodeposition of lead nanowires on a lead current collector. A polycarbonate track-etched membrane was used as a template (200 nm mean pores diameter). rGO was deposited on the nanostructured electrode from a graphene oxide (GO) dispersion in acetate buffer solution (ABS) (0.2 g/L). Potentiostatic deposition of rGO at -0.8 V vs. standard calomel electrode (SCE) was performed. Electrode with rGO was tested as negative electrode in cell with 5M sulfuric acid solution, a commercial pasted positive plate,…